Estudio del concreto de mediana a baja resistencia con microsilice nacional y aditivo plastificante, utilizando cemento Portland tipo I

Abstract

La presente investigación estudia los concretos de mediana a baja resistencia preparados con agua potable, agregado fino procedente de la cantera de Trapiche – Lima, agregado grueso procedente de la cantera de Carapongo – Huachipa, aditivo plastificante Chema plast, y adicionante Micromineral SiO 400, utilizando cemento Portland Sol tipo I, para las relaciones agua - cemento 0.70, 0.65 y 0.60. Los primeros ensayos correspondieron a la calidad de los agregados donde se determinó sus propiedades físicas, posteriormente se realizó el análisis químico del adicionante Micromineral SiO 400 y en seguida se realizaron los diseños de mezcla para el Concreto patrón (CP) con relaciones agua – cemento de 0.70, 0.65 y 0.60 para obtener Asentamientos de 4 pulgadas con el método del Peso Unitario Compactado Máximo de la combinación de los agregados; a dichos diseños se les añadió un aditivo plastificante (CPA) en cantidad de 0.35% del peso de cemento y se redujo la cantidad de agua en un porcentaje para obtener Asentamientos de 4 pulgadas; finalmente, a éstos últimos diseños se les adicionó Micromineral SiO 400 en cantidades del 5% y 10% del peso de cemento (CAM5 y CAM10). Una vez obtenido los 12 diseños de mezcla, se procedió a realizar los ensayos del concreto en estado fresco tales como: Asentamiento, Fluidez, Peso Unitario, Tiempo de fragua y Exudación; y en estado endurecido tales como: Resistencia a la compresión, Resistencia a la Tracción por compresión diametral y Módulo Elástico, resaltando los ensayos de resistencia a la compresión. Finalmente, se hace una interpretación y comparación de los resultados obtenidos, así como también un análisis de costos para los 12 diseños de mezcla.

This research studies medium to low strength concretes prepared with potable water and fine aggregate from the Trapiche - Lima quarry. The coarse aggregate from the Carapongo - Huachipa quarry. The plasticizer additive is Chema plast and Micro mineral SiO 400 is added. Portland Sol type I cement is used for the water-cement ratios 0.70, 0.65 and 0.60. The first tests correspond to the quality of the aggregates where their physical properties were determined. Subsequently, the chemical analysis of the additive Micro mineral SiO 400 was carried out. Following this, the mixture designs were made for the Standard Concrete (CP) with water-cement ratios of 0.70, 0.65 and 0.60. 4-inch settlements were obtained with the Maximum Compacted Unit Weight method of the aggregate combination. To these designs, a plasticizer additive (CPA) was added in an amount of 0.35% of the cement weight and the amount of water was reduced by a percentage to obtain 4-inch settlements. Finally, to these last designs Micro mineral SiO 400 was added in quantities of 5% and 10% of the weight of cement (CAM5 and CAM10). Once the 12 mix designs had been obtained, the tests of the concrete were carried out in a fresh state such as: Settlement, Fluidity, Unit Weight, Setting time and Exudation. In the hardened state, tests were carried out such as: Compressive Strength, Diametric Compression Tensile Strength and Elastic Modulus, highlighting the compressive strength tests. Finally, an interpretation and comparison of the obtained results is made, as well as a cost analysis for the 12 mix designs. An example of this is the use of Micro mineral SiO 400 at 5% (CAM5) and 10% (CAM10) that produces a reduction in the slump in the standard concrete with Additive (CPA) in the concrete.